The thermodynamic activities of Ni0 were studied experimentally by equilibrating Nio-Ni2+ redox in alkali nickel silicate glasses at different temperatures, melt compositions as well as different Ni0 concentrations, respectively, in air as furnace atmosphere.
Origin
Banaras Hindu University, Varanasi, India
Journal Title
Phys Chem Glasses 40 4 1999 235-241
Sector
Special Glass
Class
S 1746