Properties Of Glass-Ceramics In Li20-Al203-Si02 (Las) System With Ti02 As Nucleating Agent

A glass composition of Li20-15, Al203-11, Si02-74 wt% doped with 16 parts of Tio2 per 100 parts was melted and heat treated at 550 and 850 deg C. Thermal elongation of glass ceramics showed some discontinuity close to 300 deg C, indicating two different types of phase assemblages contributing to elongation.

Author
T R Sawhney Et Al
Origin
Banaras Hindu University, Varanasi, India
Journal Title
Trans Indian Ceramic Soc 54 6 1995 230-233